COPPER

Showing 1–12 of 26 results

  • B000001---B000003

    BRONZE BRAZING RODS BBR ( S 222 ) 1.60mm

    Code: B000001
    AWS Classification – A5.27R CuZn-C
    Used with Bronze Brazing flux and Oxygen/Acetylene Welding/Brazing, this is a highly versatile rod with has a good tensile strength. Commonly used in the motor repair industry and especially the sheet metal industry. Can also be used on galvanized iron, cast iron, copper, brass and general mild steel. This rod can be used to join similar and also dissimilar metals such as mild steel to galvanized steel, stainless steel to copper, mild steel to stainless, stainless to copper nickel and mild steel to cast iron.

    This rod has a general melting point of around the 800 degree C range and contains copper, manganese as well as silicone. Varying from supplier to supplier the rod is available in either 750mm or 1000mm lengths, in either 5Kg or 10Kg packaging.


    Read More
  • B000001---B000003

    BRONZE BRAZING RODS BBR ( S 222 ) 2.00mm

    Code: B000002
    AWS Classification – A5.27R CuZn-C
    Used with Bronze Brazing flux and Oxygen/Acetylene Welding/Brazing, this is a highly versatile rod with has a good tensile strength. Commonly used in the motor repair industry and especially the sheet metal industry. Can also be used on galvanized iron, cast iron, copper, brass and general mild steel. This rod can be used to join similar and also dissimilar metals such as mild steel to galvanized steel, stainless steel to copper, mild steel to stainless, stainless to copper nickel and mild steel to cast iron.

    This rod has a general melting point of around the 860 degree C range and contains copper, manganese as well as silicone. Varying from supplier to supplier the rod is available in either 750mm or 1000mm lengths, in either 5Kg or 10Kg packaging.


    Read More
  • B000001---B000003

    BRONZE BRAZING RODS BBR ( S 222 ) 3.20mm

    Code: B000003
    AWS Classification – A5.27R CuZn-C
    Used with Bronze Brazing flux and Oxygen/Acetylene Welding/Brazing, this is a highly versatile rod with has a good tensile strength. Commonly used in the motor repair industry and especially the sheet metal industry. Can also be used on galvanized iron, cast iron, copper, brass and general mild steel. This rod can be used to join similar and also dissimilar metals such as mild steel to galvanized steel, stainless steel to copper, mild steel to stainless, stainless to copper nickel and mild steel to cast iron.

    This rod has a general melting point of around the 890 degree C range and contains copper, manganese as well as silicone. Varying from supplier to supplier the rod is available in either 750mm or 1000mm lengths, in either 5Kg or 10Kg packaging.


    Read More
  • B000025---B000032

    COPPER TEC 0% SILVER – ROUND (BCuP-2) 2.00mm

    Code: B000025
    AWS Classification – BCuP-2
    A self fluxing, low cost copper rod containing 0% silver suitable for copper to copper or brass joints where good fit up exists. Primarily for use on copper, this alloy may also be used on other non ferrous copper based alloys. Used mainly in the refrigeration & air conditioning industry as well as electrical conductors and brass pipe fittings. Due to its phosphorous content, the rod is self fluxing on copper to copper only applications.
    This rod can be used for joining brass and bronze, however Bronze brazing flux would be required for this process.
    Melting Point: 710 Deg C
    Flowing Point: 790 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 0% SILVER – ROUND (BCuP-2) 3.00mm

    Code: B000026
    AWS Classification – BCuP-2
    A self fluxing, low cost copper rod containing 0% silver suitable for copper to copper or brass joints where good fit up exists. Primarily for use on copper, this alloy may also be used on other non ferrous copper based alloys. Used mainly in the refrigeration & air conditioning industry as well as electrical conductors and brass pipe fittings. Due to its phosphorous content, the rod is self fluxing on copper to copper only applications.
    This rod can be used for joining brass and bronze, however Bronze brazing flux would be required for this process.
    Melting Point: 710 Deg C
    Flowing Point: 790 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 15% SILVER – SILFOS 15 (BCuP-5) 2.00mm

    Code: B000031
    AWS Classification – BCuP-5
    A self fluxing, copper rod containing 15% silver suitable for copper to copper or brass joints where close fit up does not exist. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silfos 15, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 15% Ag added assists in the flow of the filler wire.
    This product is used extensively in the refrigeration. Air conditioning, electrical conductor industry where agitation, vibration and extensive movement of the joints would be subjected to. A flux should be used when using this rod to braze brass or bronze.
    Melting Point: 645Deg C
    Flowing Point: 800 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 15% SILVER – SILFOS 15 (BCuP-5) 3.00mm

    Code: B000032
    AWS Classification – BCuP-5
    A self fluxing, copper rod containing 15% silver suitable for copper to copper or brass joints where close fit up does not exist. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silfos 15, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 15% Ag added assists in the flow of the filler wire.
    This product is used extensively in the refrigeration. Air conditioning, electrical conductor industry where agitation, vibration and extensive movement of the joints would be subjected to. A flux should be used when using this rod to braze brass or bronze.
    Melting Point: 645Deg C
    Flowing Point: 800 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 2% SILVER – SILFOS 2 (BCuP-6) 2.00mm

    Code: B000027
    AWS Classification – BCuP-6
    A self fluxing, copper rod containing 2% silver suitable for copper to copper or brass joints where good fit up exists. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silbralloy or Silfos 2, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 2% Ag added assists in the flow of the filler wire.
    The optimal fill gap is a maximum of 0.2mm, the filler metal cannot be used to braze iron containing materials such as carbon, stainless steel or nickel as the phosphorous in the rod will make the joint brittle (6% Phosphorous)
    This rod is used in the refrigeration, air conditioning, electrical engineering industries like the brazing of motor rotor bars to end rings.
    Melting Point: 650 Deg C
    Flowing Point: 740 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 2% SILVER – SILFOS 2 (BCuP-6) 3.00mm

    Code: B000028
    AWS Classification – BCuP-6
    A self fluxing, copper rod containing 2% silver suitable for copper to copper or brass joints where good fit up exists. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silbralloy or Silfos 2, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 2% Ag added assists in the flow of the filler wire.
    The optimal fill gap is a maximum of 0.2mm, the filler metal cannot be used to braze iron containing materials such as carbon, stainless steel or nickel as the phosphorous in the rod will make the joint brittle (6% Phosphorous)
    This rod is used in the refrigeration, air conditioning, electrical engineering industries like the brazing of motor rotor bars to end rings.
    Melting Point: 650 Deg C
    Flowing Point: 740 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 5% SILVER – SILFOS 5 (BCuP-3) 2.00mm

    Code: B000029
    AWS Classification – BCuP-3
    A self fluxing, copper rod containing 5% silver suitable for copper to copper or brass joints where close fit up does not exist. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silfos 5, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 5% Ag added assists in the flow of the filler wire.
    This product is used extensively in the refrigeration. Air conditioning, electrical conductor industry where the gap in isn’t a tight fit. It has a good electrical conductivity and a very high tensile strength of around 250N/mm2. Most commonly used in the rewinding of electric motor copper coil industry. A flux should be used when using this rod to braze brass or bronze.
    Melting Point: 645Deg C
    Flowing Point: 710 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • B000025---B000032

    COPPER TEC 5% SILVER – SILFOS 5 (BCuP-3) 3.00mm

    Code: B000030
    AWS Classification – BCuP-3
    A self fluxing, copper rod containing 5% silver suitable for copper to copper or brass joints where close fit up does not exist. The addition of Ag assists in a lower melting temperature as well as the flow of the filler material. Often referred to in the industry as Silfos 5, the key element again is the inclusion of phosphorous. Although it increases the ductility of the filler material, it decreases the flowability of the rod, therefor the 5% Ag added assists in the flow of the filler wire.
    This product is used extensively in the refrigeration. Air conditioning, electrical conductor industry where the gap in isn’t a tight fit. It has a good electrical conductivity and a very high tensile strength of around 250N/mm2. Most commonly used in the rewinding of electric motor copper coil industry. A flux should be used when using this rod to braze brass or bronze.
    Melting Point: 645Deg C
    Flowing Point: 710 Deg C
    TIP: Surface cleaning of welding area is critical for capillary action to take place and form a solid bond.


    Read More
  • M000090

    DEOXIDIZED COPPER (ERCu) 1.20mm 12.5Kg

    Code: M000090
    AWS: A5.7 ERCu
    MIG Wire Hard Facing FC 60RC
    15Kg Plastic Spool – 1.20mm
    Deoxidized Copper is a 98% pure copper alloy for the GMAW of: Deoxidized and electrolytic tough pitch copper components. Copper castings and galvanized steels Dissimilar mild steel to deoxidized copper joints.
    Applications include the GMAW welding of copper transformer connectors, copper bus bars. Billet molds and heat elements. Repair of copper castings, low strength welding of galvanized steels and deoxidized copper to mild steel joints.
    Shielding Gas to be used – 100% Argon


    Read More